The Effect of Environment on Corrosion

The Effect of Environment on Corrosion

ABSTRACT

In this research project, the various nail was subjected to six environments to check the effect of the environments on corrosion of the nails.

Two sets of nails were used; normal nail and concrete nail. Six of each type while the other not coated.
The research was carried out in the physical-chemical laboratory of the institute of management and technology.

The environments used are the acidic solution, alkaline solution, salt solution, boiled water, air medium and lubricating oil medium, which served as a control medium.

It was observed from the graphs of the weight of metal against time, that an acidic environment gave rise to corrosion at a faster rate than another environment. It was also observed that normal nails gave rise to corrosion at a faster rate than the concrete nail.

Coating of metals was also concluded to be a method of preventing the rate of corrosion of metals even though it does not stop corrosion.

TABLE OF CONTENTS

CHAPTER ONE

INTRODUCTION

1.1 Objectives of the Study
1.2 Scope of the Study
1.3.1 Significance Of The Research

CHAPTER TWO

LITERATURE REVIEW

Historical Background
2.1 Theory of Corrosion
2.1.1 The Corrosion Process
2.1.2 Energy for the Corrosion Process
2.2 Forms Of Corrosion
2.3 Factor Affecting Corrosion Rate
2.3.1 Physical Factors Influencing Corrosion
a surface condition.
2.3.2 Environmental Factors
2.4 Corrosion Inhibitors
2.4 Electro Chemical Effects Of Corrosion
2.6 Starry Currents
2.7 Corrosion Testing Methods
2.8 Corrosion Monitoring Methods
2.8.1 Coupon Method
2.8.2 Probe Method
2.8.3 Liquid Analysis Method
2.8.4 Corrosion Products Analysis
2.8.5 Gas Analysis
2.9 Protective Coatings

CHAPTER THREE

3.0 Experimental Method
3.1 Materials/ Instrument and Tools Used
3.2 Procedure

CHAPTER FOUR

EXPERIMENTAL RESULT/OBSERVATIONS

CHAPTER FIVE

DISCUSSION

CHAPTER SIX

CONCLUSION

CHAPTER SEVEN

Recommendation

References

CHAPTER ONE

INTRODUCTION

In its broadest sense, the term corrosion is applied to the destructive alteration of a metal or alloy by chemical reaction with any substance, solid, liquid, or gas. The pattern of attack will be governed largely by the combined influence of several factors relating to the metal or alloy, the conditions of service, and the chemical nature of the environment.

1. The metal may corrode uniformly over its entire surface, as in the resting of iron in the atmosphere.

2. It may suffer only a superficial attack that does not seriously affect the strength of the metal or alloy but does discolour the surface, as in the tarnishing of silver in the atmosphere.

3. Corrosion may develop at local areas on an otherwise unattached surface, leading to pitting that may in some instances result in early failure by perforation.

4. An alloy may be attacked in such a way as to remove one or more of its constituents, leaving a weakened residue of an unattached element with poor metallic properties, as in the dezincification of yellow brass or the graphitization of cast iron.

5. Excessive corrosion may occur in the local area where poor design features tend to aggravate the corrosion conditions, as crevices under rivets, bolts and faying surface.

6. Use of dissimilar metals sometimes can lead to a severe attack of the more active metal where they are joined together.

7. High tensile stresses plus specific corrosive conditions may result in the cracking of a metal because of a corrosion reaction along critical paths in the metal.

To provide a quantitative basis for reporting corrosion rates and intensity of the attack, the average weight loss of metal per unit area per unit time or the loss in thickness per unit time is usually recorded. Loss in thickness per unit time is more useful in those instances where the engineer is concerned with the life of equipment or structure. The average loss is reported in mils per year (MPY) or inches penetration per year (py). Where product contamination is vital, the average corrosion rate is expressed in milligrams of metal corroded per square decimeter per day (mdd).

The corrosion process usually occurs because the metal tends to return to its native state, the form in which it is found in nature. This requires that the metal atoms relinquish their valence electrons to the environment and because of ions in the process. The newly formed ions may then combine with other ions from compounds. This, when iron corrodes in water, the iron atoms are converted to ferrous ions upon the loss of two electrons.

Fe Fe2++2e-

The ferrous can then combine with hydroxyl ions to form insoluble ferrous hydroxide.

Fe Fe2++20H Fe(0H)

This compound eventually becomes oxidized through content with oxygen the familiar red iron rust, ferric hydroxide. The electrons from the iron are accepted by oxygen gas molecules and iron oxides are formed.

1.1 OBJECTIVES OF THE STUDY

The objective of this study is based on the fault that corrosion which has been a major problem in our modern industries has to be prevented and curbed to the barest minimum by putting it environment into consideration in selecting material a structure or piece of equipment.

1.2 SCOPE OF THE STUDY

The main metallic material that is being used in this work is nail (iron). This material will be subjected to a different medium (environment) viz air medium salt solution medium, distilled water medium acid solution medium, alkaline solution medium and a lubricating oil medium. The observable change brought about by the environmental reaction to the material under survey was studied. The iron of varied coatings will also be used.

1.3 SIGNIFICANCE OF THE RESEARCH

A complete understanding of corrosion phenomena in all facts requires intensive and prolonged study. However, general knowledge of the subject can be gained by the engineer through a review or survey of the various ways in which corrosion manifest itself, the factors that govern the corrosion process, and the means available to the engineer for controlling or preventing corrosion.

This work will provide a survey that will serve to guide the material engineer his consideration of corrosion behaviour of metals and alloys virus, it will enable those in the oil and gas sector to install pipelines in an environment that will be favourable.