The phonon dispersion of zinc sulphide (ZnS) in zinc blende structure has been investigated using ab initio calculations based on the density functional perturbation theory within the generalized gradient approximation (GGA) of exchange correlation functional as implemented in the Quantum Espresso suite of codes. The basis functions were expanded in a plane-wave basis set with kinetic energy cut-o of 30Ryd. Brillouin zone integration was performed using 8 8 8 special k-point mesh. These k-point and energy cut-o values were tested and provide convergence of the order of milli-electron volt (meV) in self consistent calculations. To obtain the ground state properties, the zinc blende structure of zinc sulphide was optimized. Using energy-volume variation, the equilibrium lattice constant, the bulk modulus and pressure derivative of the bulk modulus were calculated with Murnaghan equation of state. The results for the structural parameters are in good agreement with avaliable theoretical and experimental values. With the lattice constant, the dynamical matrices were calculated on a uniform grid of 4 4 4 q-points mesh. The force constants in real space have been calculated using Fourier interpolation scheme which are further used for the calculation of the full phonon spectra in the entire Brillouin zone. The theoretically calculated phonon dispersion curves when compared with the avaliable experimental data and previous calculations agree fairly well. The eect of pressure on phonon dispersion of ZnS was also studied by comparing phonon frequencies of ZnS produced at pressures up to 13.4 GPa to ensure that the crystal structure remained zinc blende. Pressure dependence of all the phonon branches were investigated at the, X and L symmetry points of the Brillounin zone as well as that of longitudinal optical (LO) and transverse optical (TO) frequency splitting (LO-TO) at the same high symmetry points. The response of the phonon branches and the LO-TO frequency splitting to presure were found to follow a quadratic dependence in agreement with other theoretical calculations and experimental data.
Copyright © 2023 Author(s) retain the copyright of this article.
This article is published under the terms of the Creative Commons Attribution License 4.0
If you like this article, see others like it:
- The Effect of Pressure, Bending and Annealing Temperature on the Mechanical and Optoelectronic Properties of Perovskite Solar Cells
- The Physics of Stars and their Astronomical Identification
- The Growth and Characterization of CdS Thinfilm by Solution Technique
- Terrestrial Stability of ITO/INP Solar Cells
- Characterization of Zn/Au Back Contact to Low-doped P-InP